ASTM A90/A90M(). Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings. ASTM A ZINC PLATING WEIGHT ON STEEL. This test method covers procedures for determining the weight [mass] of coating on iron or steel sheet, wire, and. A. ASTM A90 – Standards Test Method for Weight of Coating on F. ASTM A — Steel Sheet, Zinc Coated (Galvanized) or Zinc-Iron Alloy.

Author: Taucage Sataxe
Country: Germany
Language: English (Spanish)
Genre: Video
Published (Last): 15 March 2006
Pages: 165
PDF File Size: 13.52 Mb
ePub File Size: 6.10 Mb
ISBN: 679-2-83628-695-5
Downloads: 91633
Price: Free* [*Free Regsitration Required]
Uploader: Goltishura

This requires about 15 to 30 s, except in the case of sherardized coatings, which require a somewhat longer time. The mixing should be performed under an acid fume hood. Permission rights to photocopy the standard may also be secured from the ASTM website www.

After determining the weight [mass], immerse each specimen singly in the stripping solution and allow to remain until the violent evolution of hydrogen has ceased, and only a few bubbles are being evolved.

For results to be reported in metric units, the specimen should have an area of mm2 of sheet This standard is subject to revision at any time by the responsible technical committee and must be reviewed every?

A coating of zinc on iron or steel articles provides protection against corrosion. Originally approved in See Table 1 for a statistical summary of the test results. Certain portions of the procedure involving determination of specimen weight [mass] have traditionally been performed in SI units, and corresponding inch-pound units are not included.

Determine the weight [mass] of the specimens again, to the same precision as in the initial determination. Except as otherwise provided, the specimens should have a minimum area of 3 in.

When it is not possible to determine the area accurately, as in specimens from corrugated sheets, the thickness of the stripped sheet shall be determined to the nearest 0.

  BARBONYMUS SCHWANENFELDII PDF

No further reproductions authorized. A number in parentheses indicates the year of last reapproval. Users of this standard are expressly advised that determination of the asym of any such patent rights, and the risk of infringement of such rights, are entirely their own responsibility.

ASTM A90/A90M 13镀锌和镀锌合金钢铁制品镀层重量的试验方法_百度文库

Each of ten laboratories tested three replicates of z90 different materials. In the body of this test method, reference to zinc coating shall be interpreted to also include zinc alloy coating except where speci? In the body of this test method, reference to zinc coating shall be interpreted to also include zinc alloy coating except where specifically stated otherwise. A coating of zinc on iron or steel articles provides protection against corrosion.

It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Coating weights [masses] on all zinc-coated articles other than sheets are expressed in weight [mass] per unit area of surface.

Where a continuous length is not available, shorter lengths totaling over 12 in. ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned in this standard.

If specimens were prepared to the dimensions as provided in Note 2, they shall be presumed to have an area astmm 5. Unless otherwise indicated, it is intended that all reagents shall conform to the speci?

After stripping, wash the specimens by aetm them under running water, dip in hot water, and wipe or blow dry. For very small items, several pieces may atsm to be stripped to obtain the minimum area. This standard has been approved for use by agencies of the Department of Defense. The specimen of wire may be of any length over 12 in.

A fume hood is recommended for large numbers of samples or where the test is to be carried out frequently over extended periods of time. As the protection is provided by sacri? If you feel that your comments have not received a fair hearing you should make your views known to the ASTM Committee on Standards, at the address shown below.

  DRAYTEK 2104 PDF

Since the density of the steel is known astn.

ASTM A90/A90M – 13(2018)

For specific hazards statements see 5. Specifications for zinc-coated articles frequently provide for different classes of coating so that the purchaser can select the coating weight [mass] most suitable to his needs. Alternatively, for specimens of uniform thickness of base metal, such as a piece of plate or pipe, determine the average thickness of the stripped specimen to the nearest 0.

Link to Active This link will always route to the 9a0 Active version of the standard. SR means the standard deviation for R reproducibility. Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend.

A0 comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM International Headquarters. Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard.

NOTE 2—For convenience in calculating test results in inch-pound units, the specimen should have an area of 5.

ASTM A90 – ZINC PLATING WEIGHT ON STEEL

Certain portions of the procedure involving determination of specimen weight [mass] have traditionally been performed in SI units, and corresponding inch-pound units are not included. Therefore, the test should be performed under conditions of adequate ventilation. Mixing must be done by slowly adding sulfuric acid to water due to the heat generated and possible splashing.

The same solution may be used repeatedly until the time required for stripping becomes inconveniently long.